Transition metal dichalcogenide aerogels and methods of preparation and use

ABSTRACT

Methods of forming transition metal dichalcogenide aerogels are provided. Some methods include adding at least one solvent to one or more two-dimensional transition metal dichalcogenide sheets to form a transition metal dichalcogenide solution and freeze drying the transition metal dichalcogenide solution to form frozen transition metal dichalcogenide, The methods also include heating the frozen transition metal dichalcogenide to form a transition metal dichalcogenide aerogel,

CROSS-REFERENCE TO RELATED APPLICATIONS

This Application is a Divisional under 35 U.S.C. §120 of U.S. application Ser. No. 141522,577 filed on Oct. 23, 2014, which claims priority to Indian Patent Application 4797/CHE/2013 filed on Oct. 24, 2013 and entitled “Transition Metal Dichalcogenide Aerogels and Methods of Preparation and Use” (the “First Indian Patent Application”). The disclosures of the First Indian Patent Application, including any appendices or attachments thereof, is incorporated by reference herein in its entirety.

This application is also related to U.S. patent application Ser. No. 14/520,358, filed on Oct. 22, 2014 and entitled “Two-Dimensional Transition Metal Dichalcogenide Sheets and Methods of Preparation and Use.” This related application claims priority to Indian Patent Application 4799/CHE/2013,filed on Oct. 24, 2013 and entitled “Two-Dimensional Transition Metal Dichalcogenide Sheets and Methods of Preparation and Use” (the “Second Indian Patent Application”). Both of the related application and the Second Indian Patent Application, including any appendices or attachments thereof, are incorporated by reference herein is their entirety.

BACKGROUND.

Aerogels, due to their high surface area and low densities, find applications in chemical, electronic and optical applications. For example, some aerogels are used as catalysts for synthesizing chemicals or forming electrodes in batteries and supercapacitors. Some materials that are used as aerogels include silica, graphene and carbon nanotubes. However, these aerogels are rigid, brittle in nature, crack easily when immersed in water and are expensive.

The foregoing summary is illustrative only and is not intended to be in any way limiting. In addition to the illustrative aspects, embodiments, and features described above, further aspects, embodiments, and features will become apparent by reference to the drawings and the following detailed description.

Briefly, in accordance with one aspect, a method of forming a transition metal dichalcogenide aerogel is provided. The method includes adding at least one solvent to one or more two-dimensional transition metal dichalcogenide sheets to form a transition metal dichalcogenide solution. The method also includes freeze drying the transition metal dichalcogenide solution to form frozen transition metal dichalcogenide and heating the frozen transition metal dichalcogenide to form a transition metal dichalcogenide aerogel.

In accordance with another aspect, a method of forming a transition metal dichalcogenide aerogel is provided. The method includes mixing at least one inorganic oxide with one or more two-dimensional transition metal dichalcogenide sheets to form a mixture and adding at least one solvent to the mixture to form a two-dimensional transition metal dichalcogenide solution. The method also includes freeze drying the two-dimensional transition metal dichalcogenide solution to form frozen transition metal dichalcogenide and heating the frozen transition metal dichalcogenide to form a transition metal dichalcogenide aerogel.

In accordance with another aspect, a MoS₂ aerogel is provided. The MoS₂ aerogel has an electrical conductivity of about 3.4 S/m to about to about 40 S/m.

In accordance with another aspect, a device including MoS₂ aerogel is provided. The device has an electrical conductivity of about 3.4 S/m to about 40 S/m.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 is an example flow diagram of an embodiment for a method of forming a transition metal dichalcogenide aerogel.

FIG. 2 is an example flow diagram of an embodiment for a method of forming two-dimensional transition metal dichalcogenide sheets.

FIG. 3 illustrates example images of MoS₂ aerogel.

FIG. 4 is an example image of the MoS₂ aerogel immersed in water.

FIG. 5 is an example cyclic voltammetry plot for a supercapacitor fabricated using MoS₂ aerogel.

DETAILED DESCRIPTION

In the following detailed description, reference is made to the accompanying drawings, which form a part hereof. In the drawings, similar symbols typically identify similar components, unless context dictates otherwise. The illustrative embodiments described in the detailed description, drawings, and claims are not meant to be limiting. Other embodiments may be used, and other changes may be made, without departing from the spirit or scope of the subject matter presented herein. It will be readily understood that the aspects of the present disclosure, as generally described herein, and illustrated in the figures, can be arranged, substituted, combined, separated, and designed in a wide variety of different configurations, all of which are explicitly contemplated herein.

It will also be understood that any compound, material or substance which is expressly or implicitly disclosed in the specification and/or recited in a claim as belonging to a group or structurally, compositionally and/or functionally related compounds, materials or substances, includes individual representatives of the group and all combinations thereof. While various compositions, methods, and devices are described in terms of “comprising” various components or steps (interpreted as meaning “including, but not limited to”), the compositions, methods, and devices can also “consist essentially of” or “consist of” the various components and steps, and such terminology should be interpreted as defining essentially closed-member groups.

Some embodiments are generally directed to techniques of forming transition metal dichalcogenide aerogels using two dimensional transition metal dichalcogenide sheets such as molybdenum disulphide (MoS₂ ) sheets. Such aerogels may be used in a variety of electronic devices such as supercapacitors sensors, photodetectors and batteries. The technique provides a simple and cost effective process for forming aerogels with substantially high bulk densities, resistance to fracture and high electrical conductivity. The process is easily scalable for industrial and other applications.

Referring now to FIG. 1, an example flow diagram 100 of an embodiment for a method of forming a transition metal dichalcogenide aerogel is provided. At block 102, at least one solvent is added to the one or more two-dimensional transition metal dichalcogenide sheets to form a transition metal dichalcogenide solution, In some examples, the one or more two-dimensional transition metal dichalcogenide sheets include molybdenum disulphide (MoS₂), tungsten disulphide (WS₂), titanium disulphide (TiS₂), tantalum (IV) sulphide (TaS₂), zirconium disulphide (ZrS₂), or combinations thereof. Examples of the at least one solvent include, but are not limited to, ethanol, methanol, isopropyl alcohol, or combinations thereof, in one example embodiment, a concentration of the at least one solvent is about 10 weight (wt) % to about 15 wt %. Specific examples of the concentration include about 10 wt %, about 11 wt %, about 12 wt %, about 13 wt %, about 14 wt %, about 15 wt % and ranges between any two of these values (including endpoints).

At block 104, the two-dimensional transition metal dichalcogenide solution is freeze dried to form frozen transition metal dichalcogenide. The transition metal dichalcogenide solution may be freeze dried using various techniques such as by ice bath and salt or lyophilization. In one example, the transition metal dichalcogenide solution is sonicated prior to freeze drying for a time period of about 30 minutes to about 45 minutes at a power of about 170 Watts (W) and a duty cycle of about 180 seconds/cycle. Specific examples of the sonication time include, about 30 minutes, about 35 minutes, about 40 minutes, about 45 minutes and ranges between any two of these values (including endpoints). In some examples, the transition metal dichalcogenide solution is subjected to about 10 to about 15 sonication cycles.

At block 106, the frozen transition metal dichalcogenide is heated to form a transition metal dichalcogenide aerogel, in one example embodiment, the frozen transition metal dichalcogenide is heated in an inert atmosphere at a temperature of about 175° C. to about 250° C. Specific examples of the temperature include about 175° C., about 190° C., about 205° C., about 220° C., about 235° C., about 250° C. and ranges between any two of these values (including endpoints). In some examples, the frozen transition metal dichalcogenide is heated for a time period of about 20 minutes to about 45 minutes. Specific examples of the heating time include about 20 minutes, about 25 minutes, about 30 minutes, about 35 minutes, about 40 minutes, about 45 minutes and ranges between any two of these values (including endpoints).

In certain embodiments, at least one, inorganic oxide is mixed with the one or more two-dimensional transition metal dichalcogenide sheets prior to forming the two-dimensional transition metal dichalcogenide solution (block 108). Examples of the at least one inorganic oxide include, but are not limited to, boric oxide (B₂O₃), barium oxide (BaO), praseodymium oxide (Pr₂O₃), lanthanide oxide (Ln₂O₃), manganese dioxide (MnO₂), or combinations thereof. In one example, about 0.75 milligram (mg) to about 1.5 mg of boric oxide is added to the one or more two-dimensional transition metal dichalcogenide sheets. Specific example of the mass of boric oxide includes about 0.75 mg, about 0.90 mg, about 1 mg, about 1.1 mg, about 1.2 mg, about 1.3 mg, about 1.4 mg, about 1.5 mg and ranges between any two of these values (including, endpoints).

In some examples, an electrical conductivity of the transition metal dichalcogenide aerogel formed using the above-described process is about 3.4 Siemens/meter (S/m) to about 40 S/m. Specific examples of the electrical conductivity include about 3.4 S/M, about 10 S/m, about 15 S/m, about 20 S/m, about 25 S/m, about 30 S/m, about 35 S/m, about 40 S/m and ranges between any two of these values (including endpoints). In some other examples, the transition metal dichalcogenide aerogel provides a thermal insulation at a temperature of about 1000 Kelvin (K) to about 1500 K. Specific example of the thermal insulation temperature include about 1000 K, about 1100 K, about 1200 K, about 1300 K, about 1400 K, about 1500 K and ranges between any two of these values (including endpoints).

In certain embodiments, the one or more two-dimensional transition metal dichalcogenide sheets such as MoS₂ sheets are formed by reacting a transition metal dichalcogenide with a cross-linking agent and an activating agent to form a mixture. Further, a cleaving agent is added to the mixture to form one or more contiguous transition metal dichalcogenide sheets. Referring now to FIG. 2, an example flow diagram 200 of an embodiment for a method of forming a two-dimensional transition metal dichalcogenide sheets is provided. At block 202, a cross-linking agent is added to an activating agent to form a solution. Examples of the cross-linking agent include, but are not limited to, 1-ethyl-3-[3-dimethylaminopropyl] carbodiimide hydrochloride (EDC), cystamine (C₄H₁₂N₂S₂·2HCl),N,N′-dicyclohexylcarbodiimide (DCC), 3,3′-dithiobis (sulfosuccinimidylpropionate) (DTSSP), tris(2-carboxyethyl) phosphine hydrochloride (TCEP-HCl), dithiothreitol (DTT), or combinations thereof. In one embodiment, the cross-linking agent is mixed with distilled water to form a solution prior to adding the activating agent.

In one example, a concentration of the cross-linking agent is about 33.3 millimoles (mmol) to about 66.6 mmol dissolved in about 1 milliliter (ml) of water. Specific examples of the concentration of the cross-linking agent include about 33.3 mmol, about 44.4 mmol, about 55.5 mmol, about 66 6 mmol and ranges between any two of these values (including endpoints). Examples of the activating agent include, but are not limited to ammonia (NH₃), tetramethyl ammonium hydroxide (TMAH), or combinations thereof. In one example embodiment, the pH of the activating agent is maintained at about 6.8 to about 7.1. Specific examples of the pH value include about 6.8, about 6.9, about 7.0, about 7.1 and ranges between any two of these values (including endpoints).

At block 204, a two-dimensional transition metal dichalcogenide is mixed with the above-prepared solution to form a mixture, Examples of the two-dimensional transition metal dichalcogenide include, but are not limited to, molybdenum disulphide (MoS₂), tungsten disulphide (WS₂), titanium disulphide (TiS₂), tantalum (IV) sulphide (TaS₂), zirconium disulphide (ZrS₂), bismuth telluride (Bi₂Te₃), bismuth selenide (Bi₂Se_(s)), titanium nitride chloride (TiNCI), antimony telluride (Sb₂re₃), melonite (NiTe₂), or combinations thereof In some examples, the two-dimensional transition metal dichalcogenide sheets comprise MX₂, where M is Mo, W, Bi, Sb, Ti, Pt, Nb, Ta, Ni, Zr, Hf, V, Ta, Pd, and X is S, Se, Te, NCl. In one example embodiment, mass of the two-dimensional transition metal dichalcogenide is about 25 milligrams (mg) to about 75 mg. Specific examples of the mass of the two-dimensional transition metal dichalcogenide include about 25 mg, about 35 mg, about 45 tug, about 55 mg, about 65 ma, about 75 trig, and ranges between any two of these values (including endpoints).

At block 206, a cleaving agent is added to the mixture, to form one or more contiguous sheets of transition metal dichalcogenide. Examples of the cleaving agent include, but are not limited to, N-hydroxysuccinimide (NHS), N-hydroxysulfosuccinimide (Sulfo-NHS), or combinations thereof. The cleaving agent is mixed with distilled water prior to adding the cleaving agent to the mixture. In one example, a concentration of the cleaving agent is about 33.3 millimoles (mmol) to about 66.6 mmol dissolved in about 1 milliliter (ml) of water. Specific examples of the concentration of the cross-linking agent include about 33.3 mmol, about 44.4 mmol, about 55.5 mmol, about 66.6 mmol and ranges between any two of these values (including endpoints). In this embodiment, the solution formed by adding the cleaving agent to the mixture is stirred continuously and is ultra-centrifuged to remove particulate matter such as unwanted chemicals and residues. In one example embodiment, the solution is stirred at a temperature of about 125° C. to about 200° C. Specific examples of the temperature include about 125° C., about 135° C., about 145° C., about 155° C., about 165° C., about 175° C., about 185 ° C., about 195° C., about 200° C. and ranges between any two of these values (including endpoints).

In this embodiment, the cross-linking agent such as EDC functions as a linker between chalcogen ions (such as sulphur to sulphur bond of MoS₂) of the two-dimensional transition metal dichalcogenide. Moreover, the cleaving agent such as NHS cleaves the bond between chalcogen ions (for example, sulphur) and the cross-linking agent.

At block 208, at least one solvent is added to the one or more contiguous sheets and the mixture is subsequently sonicated to remove unreacted agents. Examples of solvent include, but are not limited to, ethanol, methanol, isopropyl alcohol, or combinations thereof. In one embodiment, the mixture is sonicated for about 30 minutes, The mixture can be filtered to form multi-layered contiguous sheets of transition metal dichalcogenide. In one example, the mixture is filtered through a PVDF membrane having a pore size of about 0.2 microns.

At block 210, the one or more contiguous sheets can be exfoliated to form a plurality of two-dimensional transition metal dichalcogenide sheets. In one embodiment, the one or more contiguous sheets of transition metal dichalcogenide are exposed to electromagnetic radiation to form the plurality of two-dimensional transition metal dichalcogenide sheets. Examples of the electromagnetic radiation include, but are not limited to, thermal radiation, solar radiation, microwave radiation, or combinations thereof. In one example embodiment, the one or more contiguous sheets of transition metal dichalcogenide are heated to a temperature of about 125° C. to about 175° C. at a pressure of about 1 atmosphere (atm) to about 2 atm. Specific examples of the temperature include about 125° C., about 135° C., about 145° C., about 155° C., about 165° C., about 175° C. and ranges between any two of these values (including endpoints). Specific examples of the pressure include about 1 atm, about 1.2 atm, about 1.4 atm, about 1.6 atm, about 1.8 atm, about 2.0 atm, and ranges between any two of these values (including endpoints).

In this embodiment, the one or more contiguous sheets are exfoliated owing to substantially weak Van der Winds interactions between the layers. The solvent dispersed within the multi-layered stack of the transition metal dichalcogenide sheets is evaporated as the stack is exposed to electromagnetic radiation thereby exfoliating thin two-dimensional transition metal dichalcogenide sheets.

In some examples, an area of the MoS₂ sheets formed using, the above-described process is about 1 cm² to about 25 cm². Specific examples of the area include about 1 cm², about 5 cm², about 10 cm², about 15 cm², about 20 cm², about 25 cm², and ranges between any two of these values (including endpoints). In some other examples, a thickness of the MoS₂ sheets is about 50 nanometers to about 100 microns. Specific examples of the thickness include about 0.05 microns, about 0.1 microns, about 1 micron, about 10 microns, about 50 microns, about 100 microns and ranges between any two of these values (including endpoints). In some examples, a capacitance of the MoS₂ sheets is about 1 nanofarad (nF) to about 100 nF. Specific examples of the capacitance include about 1 nF, about 10 nF, about 30 nF, about 50 nF, about 70 nF, about 90 nF, about 100 nF and ranges between any two of these values (including endpoints).

In one example, MoS₂ aerogel is formed using the process of FIG. 1. The MoS₂ aerogel is formed by freeze drying the two-dimensional transition metal dichalcogenide solution of MoS₂ sheets and boric oxide dispersed in diluted ethanol to form frozen transition metal dichalcogenide. The frozen transition metal dichalcogenide is then heated nitrogen atmosphere. In some examples, an electrical conductivity of the formed. MoS₂aerogel is about 3.4 Siemens/meter (S/m) to about 40 S/m. Specific examples of the electrical conductivity include about 3.4 S/m, about 10 S/m, about 15 S/m, about 20 S/m, about 25 S/m, about 30 S/m, about 35 S/m, about 40 S/m and ranges between any two of these values (including endpoints).

In some other examples, the MoS₂ aerogel has a density of about 0.015 grams per cubic centimeter (g/cm³) to about 0.15 g/cm³. Specific examples of the density include about 0.015 g/cm³, about 0.03 g/cm³, about 0.06 g/cm³, about 0.09 g/cm³ about 0.15 g/cm³ and ranges between any two of these values (including endpoints). In some examples, a surface area of the MoS₂ aerogel is about 500 m²/g to about 1100 m²/g. Specific examples of the surface area include about 500 m²/g, about 600 m²/g, about 700 m²/g, about 800 m²/g, about 900 m²/g, about 1000 m²/g, about 1100 m²/g and ranges between any two of these values (including endpoints).

In some example embodiments, a device including MoS₂ aerogel is formed. Examples of the device include, but are not limited to, field-effect transistors, electrodes, sensors, photodetectors, capacitors, solar cells, light emitting diodes, thermoelectric devices, or combinations thereof. In one example, the device is a supercapacitor.

In some examples, a specific capacitance of the supercapacitor formed using the MoS₂ gel is about 2400 Farad/gram (F/g) to about 7500 F/g. Specific examples of capacitance include about 2400 F/g, about 3400 F/g, about 4400 F/g, about 5400 F/g, about 6400 F/g, about 7500 F/g and ranges between any two of these values (including endpoints). In some examples, an energy density of the supercapacitor is about 15 Watt hour/gram (Wh/g) to about 50 Wh/g. Specific examples of the energy density include about 15 Wh/g, about 20 Wh/g, about 25 Wh/g, about 30 Wh/g, about 35 Wh/g, about 40 Wh/g, about 45 Wh/g, about 50 Wh/g, and ranges between any two of these values (including endpoints).

In some other examples, a power density of the supercapacitor formed using the MoS₂ gel is about 375 Watt/kilogram (W/kg) to about 1200 W/kg. Specific examples of the power density include about 375 W/kg, about 475 W/kg, about 575 W/kg, about 675 W/kg, about 775 W/kg, about 875 W/kg, about 975 W/kg, about 1075 W/kg, about 1175 W/kg, about 1200 W/kg, and ranges between any two of these values (including endpoints).

In some examples, macroscopic three-dimensional (3D) MoS₂ aerogel assemblies are formed using the MoS₂ aerogel. Such assemblies have relatively high conductivity, high surface area and enhanced resistance to fracture as compared to other aerogels. It should be noted that the assemblies can be used in a number of consumer electronics such as structural support for batteries, supercapacitors, electrodes for batteries and sensors.

EXAMPLES

The present invention will be described below in further detail with examples and comparative examples thereof, but it is noted that the present invention is by no means intended to be limited to these examples.

Example 1 Formation of MoS₂ Sheets

MoS₂ sheets were formed using the process of FIG. 2. A biochemical buffer with about 50 ml of ammonia solution obtained from Molychem Pvt. Ltd., India was prepared and the pH of the biochemical buffer was adjusted to be about 6.9. Further, about 50 millimole 1-ethyl-3-(3-dimethylaminopropyl) carbodimide hydrochloride (EDC) obtained from Sigma-Aldrich, India was dissolved in about 1 ml of milli Q water. The above solutions were mixed and about 50 mg of amorphous molybdenum disulphide (obtained from Molychem Pvt. Ltd., India) was added and the mixture was stirred for about 10 minutes at room temperature.

Further, a solution of 50 mmol of N-hydroxysuccinimide dissolved in about 1 ml of Q water was added to the above mixture. This solution, was subsequently stirred for 6 hours at a temperature of about 150° C. Here, EDC acted. as a linker between sulphur to sulphur atoms of MoS₂ whereas NHS acted as a cleaving agent and cleaved the bond between sulphur and EDC, thereby combining the two sulphurs. The above solution was washed with milli Q water and was ultra-centrifuged to remove unwanted chemicals and residues. Next, about 50 ml of ethanol was added and the solution was sonicated for about 10 minutes and filtered through polyvinylidene difluoride (PVDF) membrane having a pore size of about 0.2 microns. The membrane was removed and the filtrate was heated at a temperature of about 50° C. for about 10 minutes to separate the MoS₂ multilayered stack from the PVDF membrane.

Example 2 Characterization of the MoS₂ Sheets

The multilayered MoS₂ sheets of Example 1 were characterized using a colorimeter for sulphide-sulphide bond continuity. Here, colorimetric assay using reagent 2-nitro-5-thiosulfobenzoate was used for determination of disulfide bond. The color of the formed crystal was observed to be light green, which indicated that the bonds were continuous. The multi-layered MoS₂ stack had a continuous surface that indicated that the sheets were continuous. The thickness of the multi-layered MoS₂ sheets was measured to be about 3.5 microns.

Example 3 Exfoliation of MoS₂ Sheets

The multi-layered MoS₂ stacked sheets of Example 1 were thermally exfoliated to obtain molybdenum disulphide (MoS₂) sheets, The multi-layered MoS₂ sheets were transferred to a stainless steel vessel and were induction heated to a temperature of about 50° C. containing air at about 1 atm, pressure for about 10 minutes to about 15 minutes. Subsequently, the temperature was raised to about 150° C. and was maintained at about 150° C. for a time period of about 5 minutes to about 6 minutes. Here, ethanol dispersed within the MoS₂ multilayered stacks was evaporated due to the induction heat and resulted in exfoliation of MoS₂ multi-layered stacks to thin MoS₂ sheets having a thickness of about 3.5 microns.

Example 4 Characterization of the Exfoliated MoS₂ Sheets

The exfoliated MoS₂ sheet was observed to be transparent. Here, the electrical resistivity of the sample was measured using the standard four probe technique and was estimated to be about 222.5 ohm centimeters (Ωcm). Further, the specific capacitance of the sample was measured to be about 1.29 nano Farad (nF).

Example 5 Formation of MoS₂ Aerogel

The MoS₂ aerogel was formed using the example process of FIG. 1. The MoS₂ sheet weighing about 1 g was mixed with about 1 mg of boric oxide and the mixture was dispersed in about 10 ml of ethanol diluted with about 90 ml of DI water to form a solution. This solution was sonicated for a time period of about 30 minutes with a power factor of about 170 W and a duty cycle of about 180 s/cycle to obtain consistency. The above solution was then freeze dried using ice bath and salt. After freeze drying, the sample was transferred to a quartz boat and was heated at a temperature of about 200° C. for a time period of about 30 minutes in a closed furnace.

Example 6 Characterization of the MoS₂ Aerogel

The MoS₂ aerogel of Example 5 was characterized for its physical properties such as surface area, thermal insulation, and deformation under weight. FIG. 3 illustrates images 300 of the MoS₂ aerogel formed using the process of Example 5. The images 302, 304, 306 and 308 represent the images obtained at resolutions of 20×, 20×a, 400×and 400×a respectively. The percentage of solids in the MoS₂ aerogel was estimated to be about 0.1% to about 15%.

The MoS₂ aerogel was also exposed to a commercially available cigarette lighter to evaluate its thermal insulation properties. The MoS₂ aerogel was exposed to a temperature of about 1000 K to about 1500 K for about 30 minutes and no degradation was observed implying the thermal insulation at these temperatures. Further, surface area determination for the MoS₂ aerogel was performed using Brunauer-Immett-Teller (BET) method in nitrogen atmosphere. The MoS₂ aerogel weighing about 0.1 g was heated to a temperature of about 150° C. under vacuum at a pressure of about 10 Torr to about 15 Torr for a time period of about 24 hours to remove all the adsorbed species. The surface area of the MoS₂ aerogel without boric oxide determined using BET method for different initial weights is provided in Table 1:

TABLE 1 Initial Final Temperature weight Time Pressure weight BET SA m²/g ° C. Process (g) a (hour) (psi) (g) b (b − a) * 2 * 980.67 30 Absorption 0.5 1 30 0.76 549.17 100 Desorption 0.76 1 30 0.53 450.10 30 Absorption 0.5 2 30 0.84 666.85 100 Desorption 0.84 2 30 0.55 568.78 30 Absorption 0.5 3 30 0.86 706.08 100 Desorption 0.86 3 30 0.55 617.82

The bulk densities of the MoS₂ aerogel were determined from physical dimensions and mass of each sample and were estimated to be about 0.02 g/cm³ to about 0.15 g/cm³. The bulk density of the MoS₂ aerogel was observed to be relatively higher than the density of silica aerogel owing to relatively high molecular weight of molybdenum and sulphur. Moreover, brittle strength of the formed MoS₂ aerogel was evaluated. The MoS₂ aerogel of Example 5 was immersed in water for a time period of about 30 minutes. FIG. 4 is an example image 400 of the MoS₂ aerogel immersed in water. The weight of the sample was measured before and after immersion, and it was observed to be substantially same implying that the MoS₂ aerogel remained intact within the water thus exhibiting resistance to cracks when exposed to water.

Example 7 Electrical Properties of the MoS₂ Aerogel

The bulk electrical conductivity of the MoS₂ aerogel was measured using four-probe method with metal electrodes attached to the ends of samples using silver paste. The bulk electrical conductivity of the MoS₂ aerogel was measured to be about 40 S/m for pure MoS₂ aerogel and about 3.4 S/m for MoS₂ gel having about 0.1 wt % of boric oxide. The relatively higher values of conductivity were observed due to substantially large reduction in resistance at the junctions between MoS₂ sheets. The physical properties for the MoS₂ aerogel with and without boric oxide are provided in Table 2:

TABLE 2 Initial BET wt % surface Electrical boric Density area conductivity oxide g/cm³ (m²/g) (S/m) 0 0.112 649 40 0.1 0.015 1167 3.44

Example 8 Fabrication of Supercapacitor using MoS₂ Aerogel

A supercapacitor was fabricated using the MoS₂ aerogel formed using the present technique. Here, about 1.150 mg of chemically and thermally exfoliated MoS₂ sheets were dispersed in about 750 111 of Nafion solution by sonication. The mixture of the MoS₂ sheets and the Nafion solution was sonicated for about 3 minutes. Two pieces of carbon cloth having an area of about 2 cm×2 cm were heated at a temperature of about 100° C. The solution formed by dispersing the MoS₂ sheets in Nafion solution was sprayed on the heated carbon cloths and then the carbon cloths were dried for about 5 minutes.

Further, about 3 g of polyvinyl alcohol (PVA) was dissolved in about 100 ml of DI water and the resultant solution was dried in a petri dish to form a PVA film. The PVA film was placed between the two carbon cloths to form the supercapacitor.

Example 9 Characterization of the Supercapacitor of Example 8

The performance of the supercapacitor of Example 7 formed using MoS₂ aerogel was evaluated using cyclic voltammetry. FIG. 5 is a graphical representation of cyclic voltammetry results 500 for the supercapacitor of Example 7. As can be seen from the cyclic voltammetry plot, the proposed supercapacitor provides a wide operating potential of about +3 volts to about −2 volts for storing charge shown by reference numerals 502 and 504 respectively.

Moreover, the specific capacitance of the supercapacitor was estimated to be about 2400 F/g to about 7500 F/g and the energy density of the supercapacitor was estimated to be about 15 Wh/g to about 50 Wh/g. Further, the power density of the supercapacitor was estimated to be about 375 W/kg to about 1200 W/kg.

The present disclosure is not to be limited in terms of the particular embodiments described in this application, which are intended as illustrations of various aspects. Many modifications and variations can be made without departing from its spirit and scope, as will be apparent to those skilled in the art. Functionally equivalent methods and apparatuses within the scope of the disclosure, in addition to those enumerated herein, will be apparent to those skilled in the art from the foregoing descriptions. Such modifications and variations are intended to fall within the scope of the appended claims.

The present disclosure is to be limited only by the terms of the appended claims, along with the full scope of equivalents to which such claims are entitled. It is to be understood that this disclosure is not limited to particular methods, reagents, compounds compositions or biological systems, which can, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular embodiments only, and is not intended to be limiting.

With respect to the use of substantially any plural and/or singular terms herein, those having skill in the art can translate from the plural to the singular and/or from the singular to the plural as is appropriate to the context and/or application. The various singular/plural permutations may be expressly set forth herein for sake of clarity.

It will be understood by those within the an that, in general, terms used herein, and especially in the appended claims (for example, bodies of the appended claims) are generally intended as “open” terms (for example, the term “including” should be interpreted as “including but not limited to,” the term “having” should be interpreted as “having at least,” the term “includes” should be interpreted as “includes but is not limited to,” etc.). It will be further understood by those within the art that if a specific number of an introduced claim recitation is intended, such an intent will be explicitly recited in the claim, and in the absence of such recitation, no such intent is present.

For example, as an aid to understanding, the following appended claims may contain usage of the introductory phrases “at least one” and “one or more” to introduce claim recitations. However, the use of such phrases should not be construed to imply that the introduction of a claim recitation by the indefinite articles “a” or “an” limits any particular claim containing such introduced claim recitation to embodiments containing only one such recitation, even when the same claim includes the introductory phrases “one or more” or “at least one” and indefinite articles such as “a” or “an” (for example, “a” and or “an” should be interpreted to mean “at least one” or “one or more”); the same holds true for the use of definite articles used to introduce claim recitations.

In addition, even if a specific number of an introduced claim recitation is explicitly recited, those skilled in the art will recognize that such recitation should be interpreted to mean at least the recited number (for example, the bare recitation of “two recitations,” without other modifiers, means at least two recitations, or two or more recitations). Furthermore, in those instances where a convention analogous to “at least one of A, B, and C, etc.” is used, in general such a construction is intended in the sense one having skill in the art would understand the convention (for example, “a system having at least one of A, B, and C” would include but not be limited to systems that have A alone, B alone, C alone, A and B together, A and C together, B and C together, and/or A, B, and C together, etc.). In those instances where a convention analogous to “at least one of A, B, or C, etc.” is used, in general, such a construction is intended in the sense one having skill in the art would understand the convention (for example, “a system having at least one of A, B, C” would include but not be limited to systems that have A alone, B alone, C alone, A and B together, A and C together, B and C together, and/or A, B, and C together, etc.).

It will be further understood by those within the art that virtually any disjunctive word and/or phrase presenting two or more alternative terms, whether in the description, claims, or drawings, should be understood to contemplate the possibilities of including one of the terms, either of the terms, or both terms. For example, the phrase “A or B ” will be understood to include the possibilities of “A” or “B” or “A and B”.

As will be understood by one skilled in the art, for any and all purposes, such as in terms of providing a written description, all ranges disclosed herein also encompass any and all possible sub ranges and combinations of sub ranges thereof. Any listed range can be easily recognized as sufficiently describing and enabling the same range being broken down into at least equal halves, thirds, quarters, fifths, tenths, etc. As a non-limiting example, each range discussed herein can be readily broken down into a lower third, middle third and upper third, etc,

As will also be understood by one skilled in the art all language such as “up to,” “at least,” “greater than,” “less than,” and the like include the number melted and refer to ranges which can be subsequently broken down into sub ranges as discussed above. Finally, as will be understood by one skilled in the art, a range includes each individual member. Thus, for example, a group having 1-3 cells refers to groups having 1, 2, or 3 cells. Similarly, a group having 1-5 cells refers to groups having 1, 2, 3, 4, or 5 cells, and so forth. While various aspects and embodiments have been disclosed herein, other aspects and embodiments will be apparent to those skilled in the art. The various aspects and embodiments disclosed herein are for purposes of illustration and are not intended to be limiting, with the true scope and spirit being indicated by the following claims. 

We claim:
 1. A molybdenum disulphide (MoS₂) aerogel, the MoS₂ aerogel having an electrical conductivity of about 3.4 S/m to about to about 40 S/m, a density of the aerogel is about 0.015 g/cm³ to about 0.15 g/cm³ and as surface area of the aerogel is about 500 m²/g to about 1100 m²/g.
 2. The MoS₂ aerogel of claim 1, wherein the aerogel is formed by freeze drying a two-dimensional transition metal dichalcogenide solution of MoS₂ sheets and boric oxide dispersed in a solvent to form frozen transition metal dichalcogenide and heating the frozen transition metal dichalcogenide in an inert atmosphere.
 3. The MoS₂ aerogel of claim 1, wherein each of the MoS₂ sheets have an area of about 1 cm² to about 25 cm².
 4. A device comprising molybdenum disulphide (MoS₂) aerogel, the MoS₂ aerogel having an electrical conductivity of about 3.4 S/m to about 40 S/m.
 5. The device of claim 4, wherein the device comprises field-effect transistors, electrodes, sensors, photodetectors, capacitors, solar cells, light emitting diodes, thermoelectric devices, or combinations thereof.
 6. The device of claim 5, wherein the device comprises to supercapacitor having a specific capacitance of about 2400 F/g to about 7500 F/g, an energy density of about 15 Wh/g to about 50 Wh/g, and a power density of about 375 W/kg to about 1200 W/kg.
 7. The MoS₂ aerogel of claim 2, wherein the heating of the frozen transition metal dichalcogenide is performed at a temperature of about 175° C. to about 250° C.
 8. The MoS₂ aerogel of claim 2, further comprising the reaction of MoS₂ with a cross-linking agent and an activating agent to form a mixture and adding a cleaving agent to the mixture to form at least one or more contiguous sheets of MoS₂.
 9. The MoS₂ aerogel of claim 8, wherein the cross-linking agent comprises 1-ethyl-3-[3-dimethylaminopropyl]carbodiimide hydrochloride (EDC), cystamine (C₄H₁₂N₂S₂-2HCl), N,N′-dicyclohexylcarbodiimide (DCC), 3,3′-dithiobis(sulfosuccinimidylpropionate) (DTSSP), tris(2-carboxyethyl) phosphine hydrochloride at (TCEP-HCl), dithiothreitol (DTT), or combinations thereof.
 10. The MoS₂ aerogel of claim 8, wherein the activating agent comprises ammonia (NH³), tetramethyl ammonium hydroxide (TMAH), or combinations thereof.
 11. The MoS₂ aerogel of claim 8, wherein the cleaving agent comprises N-hydroxysuccinimide (NHS), N-hydroxysulfosuccinimide (Sulfo-NHS), or combinations thereof.
 12. The MoS₂ aerogel of claim 8, further comprising exfoliating, the at least one or more contiguous sheets of MoS₂ to form a plurality of two dimensional transition metal dichalcogenide of MoS₂ sheets.
 13. The MoS₂ aerogel of claim 12, wherein exfoliating the at least one or more contiguous sheets of MoS₂ by electromagnetic radiation.
 14. The MoS₂ aerogel of claim 13, wherein the electromagnetic radiation comprises thermal radiation, solar radiation, microwave radiation, or combinations thereof.
 15. The MoS₂ aerogel of claim 2, further comprising sonicating the two-dimensional transition metal dichalcogenide solution of MoS₂ sheets prior to freeze drying the solution.
 16. The MoS₂ aerogel of claim 15, wherein the two-dimensional transition metal dichalcogenide solution of MoS₂ sheets is sonicated for about 30 minutes to about 45 minutes.
 17. The MoS₂ aerogel of claim 15, wherein the two-dimensional transition metal dichalcogenide solution of MoS₂ sheets is sonicated at a power of about 170 Watts (W) and a duty cycle of about 180 s/cycle.
 18. The MoS₂ aerogel of claim 2, wherein freeze drying the two-dimensional transition metal dichalcogenide solution of MoS₂ sheets comprises freezing the solution using ice bath and salt, lyophilization or combinations thereof.
 19. A supercapacitor comprising molybdenum disulphide (MoS₂) aerogel having an electrical conductivity of about 3.4 S/m to about 40 S/m, the MoS₂ aerogel comprising exfoliated MoS₂ sheets, the exfoliated sheets dispersed in a solution by sonication.
 20. The supercapacitor of claim 19, wherein the solution formed by dispersing the exfoliated MoS₂ sheets is sprayed on a heated carbon cloth. 